Terms used in the Metals Industry
There are 182 entries in this glossary.B
| Term | Definition | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Beryllium copper |
Copper Alloys C17200, C17300, C17500, and C17510 Beryllium copper, also known as copper beryllium, CuBe or beryllium bronze, is a metal alloy of copper and 0.5 to 3% beryllium, and sometimes with other alloying elements, and has significant metalworking and operating performance qualities.
Chemical Composition for C17200
Chemical Composition for C17300
Chemical Composition for C17500
Chemical Composition for C17510
|
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Billet |
A hot-worked semifinished product suitable for subsequent working by such methods as rolling, forging, extruding, etc. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Blank |
A piece from any wrought product intended for subsequent fabrication by such operations as forming, bending, cupping, drawing, hot pressing. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Blanking |
The process of cutting metal blanks by a die and punch set in a press, or by sawing or shearing. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Blister |
A raised spot on the surface of the metal caused by expansion of gas in subsurface zone during thermal treatment. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Block Marks |
Short longitudinal scratches introduced during rewinding of sheet or foil, resulting from relative movement between adjacent wraps of the coil. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Bloom |
A semifinished hot rolled product, rectangular or square in cross section produced on a blooming mill. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| BMS |
A prefix for Boeing's material specifications. Ex: BMS-7-28 equals E- 4340 MOD V.M., E-4340 N&T |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Bottom Draft |
Taper or slope in the bottom of a forged depression to assist the flow of metal toward the sides of the depressed area. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Bow |
Longitudinal curvature of rod, bar, shapes, and tube. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Brass |
Any copper alloy with zinc as the principal alloying element, with or without small quantities of some other elements. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Brazing |
A joining process wherein coalescence is produced by heating to suitable temperatures above 800 F. and by using a non-ferrous filler metal having a melting point below that of the base metals. The filler metal is distributed between the closely fitted surfaces of the joint by capillary attraction. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Brazing Rod |
A rolled, extruded, or cast round filler metal for use in joining by brazing. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Brazing Sheet |
Sheet of a brazing alloy or sheet clad with a brazing alloy on one or both sides. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Brazing Wire |
Wire for use as a filler metal in joining by brazing. |